Stainless Steel Sprocket Nut M12 x (1.50mm)

Stainless Steel Sprocket Nut M12 x (1.50mm)
exc VAT £4.18 inc VAT £5.02
Part Number: MLSSSPN12C
exc VAT £4.18 inc VAT £5.02


Manufactured using Aerospace High Tensile Anodised Aluminium then fitted with a steel helicoil for additional strength. Supplied with fitment instructions which specify a lower torque setting of 33ft/lb or 44 Newton Metres. Nuts have a 19mm Socket Size. Nuts have a flange diameter of 24mm

Additional Information

Material Stainless
Product Type Sprocket
Weight in Gms 10.6000
Country of Manufacture United Kingdom
Thread Diameter 12mm
Thread Pitch 1.50mm
Outside Diameter 20mm
Height 12.30mm
Socket Size 15mm
Pack Quantity 1

Material Information 

Stainless Steel

Manufactured from A316 stainless steel. A316 stainless steel has a minimum chromium content of 16.5% and contains elements of carbon, molybdenum, silicon, phosphorus, sulphur, nickel, manganese and iron, all of which add properties of formability, strength, weldability and enhanced corrosion resistance. All of the fasteners are highly polished to a mirror-like finish.

  • Density 8030kg/m3 (501lb/ft3)
  • Young's Modulus 193GPa (28 x 106psi)
  • Yield Strength 260MPa (37.7 x 103)
  • Ultimate Tensile Strength 570MPa (82.7 x 103 psi)
  • Compressive Strength 260MPa (37.7 x 103 psi)
  • Shear Modulus78GPa (11.3 x 106 psi)
  • Ductility 40% elongation at break +
  • Minimum value allowed by ASTMA240
  • Poisson's Ratio0.27
  • Hardness 95 Rockwell B+
  • Maximum value allowed by ASTMA240
  • Strength-to-Weight Ratio 32.4 kNm/kg
  • Stiffness-to-Weight Ratio 24.0 Mnm/kg

Black & Gold Stainless Steel: Long lasting finish resulting from an application of Diamond Like Coating (DLC). This unique finish increases the fastener lifetime and helps to prevent galling whilst providing a supreme hardness and offering the optimum in corrosion resistance thanks to a nanocomposite coating.